Effect of dentin preparation mode on the bond strength between human dentin and different resin cements

Abstract The aim was to evaluate the influence of different dentin preparation mode in the smear layer characteristics (SL), hybrid layer (HL), and microtensile bond strength (µTBS) to dentin with two resin cements. The occlusal dentin of 120 third molars was exposed. The teeth were divided into 4 groups (n=30) according to the dentin preparation mode: 1- fine grain diamond bur; 2- coarse grain diamond bur; 3- multi laminate carbide steel bur; and, 4- ultrasonic CV Dentus diamond bur. Each treated dentin group was divided into 2 sub-groups (n=15) according to the resin cement: (1) RelyX U200 and (2) RelyX ARC. Resin composite blocks were cemented on dentin. After storage at 37o C for 24 h, beams with a cross section area of 1.0 mm2 were obtained, and tested in a universal testing machine at a crosshead speed of 0.5 mm/min. Two additional teeth for each sub-group were prepared to analyze the SL and HL on a scanning electron microscopy. According to Kruskal-Wallis test and Dunn tests, there was no significant difference in µTBS among the rotary instruments within each resin cement group. RelyX ARC obtained higher µTBS values compared to RelyX U200 (p<0.05). RelyX ARC formed evident HL, which was not observed for RelyX U200. The dentin mode preparation did not influence the µTBS of the resin cements. The SL was different for all instruments. The cementing agent is more determinant in the hybrid layer formation and bond strength to dentin than the instruments applied on dentin.

Resumo O objetivo deste estudo foi avaliar a influência de diferentes modos de preparação da dentina nas características da smear layer (SL), da camada híbrida (CH) e na resistência de união à microtração (RUµT) à dentina com dois cimentos resinosos. A dentina oclusal de 120 terceiros molares humanos foi exposta. Os dentes foram divididos em 4 grupos (n=30) de acordo com o modo de preparação da dentina: 1 - ponta diamantada de granulação fina; 2 - ponta diamantada de granulação grossa; 3 - ponta de carboneto de aço multilaminada; 4 - ponta diamantada ultrassônica. Cada grupo foi subdividido em dois subgrupos (n=15) de acordo com o cimento resinoso: (1) RelyX U200 e (2) RelyX ARC. Blocos de resina composta foram cimentados na dentina. Após armazenamento a 37 °C por 24 h, as amostras foram cortadas para obter palitos com área de 1,0 mm2, os quais foram testados em máquina de ensaio universal com velocidade de 0,5 mm/min. Dois dentes adicionais por subgrupo foram preparados para analisar as características da SL e da CH em microscópio eletrônico de varredura. De acordo com o teste de Kruskal-Wallis e o teste de Dunn, não houve diferença significativa na RUµT entre os instrumentos rotatórios para cada cimento resinoso. RelyX ARC obteve maiores valores de RUµT em comparação ao RelyX U200 (p<0,05). RelyX ARC formou uma CH evidente, o que não foi observado para o RelyX U200. O modo de preparação da dentina não influenciou na RUµT dos cimentos resinosos. A SL foi diferente para todos os instrumentos. O agente de cimentação foi mais determinante na formação da camada híbrida e na resistência de união do que os instrumentos utilizados para preparar a dentina.

Prototype to measure bracket debonding force in vivo

ABSTRACT Introduction: Material biodegradation that occurs in the mouth may interfere in the bonding strength between the bracket and the enamel, causing lower bond strength values in vivo, in comparison with in vitro studies. Objective: To develop a prototype to measure bracket debonding force in vivo and to evaluate, in vitro, the bond strength obtained with the prototype. Methods: A original plier (3M Unitek) was modified by adding one strain gauge directly connected to its claw. An electronic circuit performed the reading of the strain gauge, and the software installed in a computer recorded the values of the bracket debonding force, in kgf. Orthodontic brackets were bonded to the facial surface of 30 bovine incisors with adhesive materials. In Group 1 (n = 15), debonding was carried out with the prototype, while tensile bond strength testing was performed in Group 2 (n = 15). A universal testing machine was used for the second group. The adhesive remnant index (ARI) was recorded. Results: According to Student’s t test (α = 0.05), Group 1 (2.96 MPa) and Group 2 (3.08 MPa) were not significantly different. ARI score of 3 was predominant in the two groups. Conclusion: The prototype proved to be reliable for obtaining in vivo bond strength values for orthodontic brackets.

RESUMO Introdução: a biodegradação de materiais que ocorre na cavidade bucal pode interferir na resistência de união entre o braquete e o esmalte, causando baixos valores de resistência de união in vivo, em comparação aos valores in vitro. Objetivo: o objetivo do presente estudo foi desenvolver um protótipo para mensurar, in vivo, a força de descolagem de braquetes e avaliar, in vitro, a resistência de união obtida com o uso do protótipo. Métodos: um alicate (3M Unitek) foi modificado por meio da adição de um extensômetro diretamente conectado à garra do alicate. Um circuito eletrônico realizou a leitura do extensômetro, e um software instalado em um computador registrou os valores de força de descolagem do braquete em kgf. Os braquetes ortodônticos foram colados com material adesivo na face vestibular de 30 dentes incisivos bovinos. No Grupo 1 (n = 15), a descolagem foi realizada com o protótipo, enquanto no Grupo 2 (n = 15) foi realizado teste de resistência de união à tração, utilizando-se uma máquina universal de ensaios. O índice de adesivo remanescente (ARI) foi analisado. Resultados: de acordo com o teste de t de Student (α = 0,05), os grupos 1 (2,96 MPa) e 2 (3,08 MPa) não foram estatisticamente diferentes. O escore 3 do ARI foi predominante nos dois grupos. Conclusão: o protótipo mostrou-se confiável para se obter, in vivo, os valores de resistência de união dos braquetes ortodônticos.

Improving adhesion between luting cement and zirconia-based ceramic with an alternative surface treatment

This study evaluated the influence of an alternative surface treatment on the microshear bond strength (μsbs) of zirconia-based ceramic. Thirty-five zirconia disks were assigned to five groups according to the following treatments: Control (CO), glass and silane were not applied to the zirconia surface; G1, air blasted with 100μm glass beads + glaze + silane; G2, a gel containing 15% (by weight) glass beads applied to the ceramic surface + glaze + silane; G3, a gel containing 25% (by weight) glass beads applied to the ceramic surface + glaze + silane; and G4, a gel containing 50% (by weight) glass beads applied to the ceramic surface + glaze + silane. The specimens were built up using RelyX ARC®, according to the manufacturer’s recommendations, and inserted in an elastomeric mold with an inner diameter of 0.8 mm. The μsbs test was performed using a testing machine at a crosshead speed of 0.5 mm/min. ANOVA and Tukey’s test (p < 0.05) were applied to the bond strength values (in MPa). CO (15.6 ± 4.1) showed the lowest μsbs value. There were no statistical differences between the G1 (24.9 ± 7.4), G2 (24.9 ± 2.3), G3 (35.0 ± 10.3) and G4 (35.3 ± 6.0) experimental groups. Those groups submitted to surface treatments with higher concentrations of glass showed a lower frequency of adhesive failures. In conclusion, the glass application improved the interaction between the ceramic and the luting cement.

Dentin Bond Strength of a Fluoride-Releasing Adhesive System Submitted to pH-Cycling

To evaluate the microtensile bond strength (µTBS) of a fluoride-containing adhesive system submitted to a pH-cycling and storage time regimen for primary outcomes. As secondary outcomes the fluoride released amount was evaluated. Twelve dentin surfaces from sound third molar were divided into 2 groups according to adhesive systems: Clearfil SE Protect (PB) and Clearfil SE Bond (SE). Sticks obtained (1.0 mm2) from teeth were randomly divided into 3 subgroups according to storage regimen model: immediate (24h); 5-month deionized water (W); and pH-cycling model (C). All sticks were tested for µTBS in a universal testing machine. Fluoride concentration was obtained from 1-4 days and 30-day in W and 1-4 days in demineralization (DE)/remineralization (RE) solutions from C, using a fluoride-specific electrode. µTBS and fluoride released data were, respectively, submitted to ANOVA in a split plot design and Tukey, and Friedman' tests (a=0.05). There was no significant interaction between adhesive system and storage regimen for µTBS. W showed the lowest µTBS values. There was no significant difference between 24 h and C models for µTBS. There was no significant difference between adhesive systems. Failure mode was predominantly cohesive within composite for the 24 h and W, for the C group it was mixed for SE and cohesive within composite for PB adhesive system. Fluoride concentrations in the DE/RE solutions were less than 0.03125 ppm and not detected in W. In conclusion, the fluoride-containing adhesive system performed similarly to the regular one. Hydrolytic degradation is the main problem with both adhesive systems, regardless of fluoride contents.

O objetivo principal desse estudo foi avaliar a resistência de união à microtração de dois sistemas adesivos (com e sem flúor) após a ciclagem de pH e armazenagem em água deionizada. A quantidade de flúor liberada foi avaliada secundariamente. Doze terceiros molares hígidos foram separados em 2 grupos de acordo com o sistema adesivo: Clearfil SE Protect - com flúor (PB) e Clearfil SE Bond - sem flúor (SE). Os palitos (1 mm2) obtidos do mesmo dente foram aleatoriamente divididos em 3 subgrupos de acordo com o meio de armazenagem: em água deionizada por 24h ou 5 meses e ciclagem de pH. Os palitos foram tracionados em uma máquina de ensaio universal a 0,5 mm/min. A concentração de flúor foi analisada em água deionizada (1-4 dias e 30 dias) e na solução remineralizadora e desmineralizadora (1-4 dias) usando um eletrodo específico. Os dados de resistência de união e liberação de flúor foram, respectivamente, submetidos à Análise de Variância em esquema de parcela subdividida e ao teste de Friedman (a=0,05). Não houve nenhuma interação significativa na resistência de união entre os sistemas adesivos e os meios de armazenagem. Os menores valores de resistência de união à microtração foram encontrados para os palitos armazenados em água deionizada. Não houve nenhuma diferença significativa nos valores de resistência de união após 24h e ciclagem de pH. Nenhuma diferença significativa na resistência de união foi observada entre os 2 sistemas adesivos. O modo de falha foi predominantemente coesivo em compósito para os grupos armazenados em água por 24h ou 5 meses para ambos os sistemas adesivos. No grupo submetido à ciclagem, a falha foi mista para o SE e coesiva em compósito para o PB. A concentração de flúor nas soluções DE/RE foi menor que 0,03125 ppm e não detectada em água deionizada. Concluindo, o sistema adesivo com flúor (PB) apresentou performance similar ao sistema adesivo sem flúor (SE). A degradação hidrolítica foi o principal fator para ambos os sistemas adesivos, independente da adição de flúor.

Sistema NAS: Nursing Activities Score em tecnologia móvel / The NAS System: Nursing Activities Score in mobile technology / Sistemas NAS: Nursing Activities Score (NAS) en tecnología móvil

Este estudo objetivou apresentar a estrutura informatizada que viabiliza a utilização do Nursing Activities Score (NAS) em tecnologia móvel. Trata-se de um projeto de desenvolvimento de produção tecnológica baseado na engenharia de software, fundamentada na teoria do ciclo de vida de desenvolvimento de sistema. O Sistema NAS foi construído em dois módulos: módulo de pesquisa, cujo acesso é realizado através de computador pessoal (PC) e módulo de coleta de dados, acessado por meio de dispositivo móvel (smartphone). O Sistema NAS foi construído de modo a permitir que outros formulários, além do instrumento NAS, sejam incluídos futuramente. Assim, entende-se que o desenvolvimento do Sistema NAS permitirá a aproximação entre os enfermeiros e a tecnologia móvel facilitando o acesso imediato aos dados do instrumento referentes aos pacientes, auxiliando na tomada de decisão e na adequação do quantitativo de pessoal de enfermagem para prestação da assistência.

The objective of this study was to present the computerized structure that enables the use of the Nursing Activities Score (NAS) in mobile technology. It is a project for the development of technology production based on software engineering, founded on the theory of systems development life cycle. The NAS system was built in two modules: the search module, which is accessed using a personal computer (PC), and Data Collection module, which is accessed through a mobile device (Smartphone). The NAS system was constructed to allow other forms, in addition to the NAS tool, to be included in the future. Thus, it is understood that the development of the NAS will bring nurses closer to mobile technology and facilitate their accessibility to the data of the instrument relating to patients, thus assisting in decision-making and in staffing to provide nursing care.

Estudio que objetivó presentar la estructura informatizada que viabiliza la utilización del Nursing Activities Score (NAS) en tecnología móvil. Se trata de un proyecto de desarrollo de producción tecnológica basado en ingeniería de software, fundamentada en la teoría del ciclo de vida de desarrollo de sistema. El sistema NAS se construyó en dos módulos: módulo de Investigación, con acceso a través de computadora personal (PC) y módulo de Recolección de Datos, donde se utiliza un dispositivo móvil (Smartphone). El sistema NAS se desarrolló de modo que permita que otros formularios, además del instrumento NAS, se incluyan a futuro. Se entiende que el desarrollo del Sistema NAS permitirá la aproximación entre los enfermeros y la tecnología móvil, facilitando el acceso inmediato a los datos del instrumento referentes a los pacientes, auxiliando en la toma de decisiones y en la adecuación de cantidad de personal de enfermería necesario para brindar la asistencia.

Influence of ceramic primers on microshear bond strength between resin cements and zirconia-based ceramic

This study evaluated the effect of a coupling agent ceramic primer (CP) on the microshear bond strength (ìsbs) between luting cements and zirconia-based ceramic. Methods: Zirconia discs (Cercon) were made and finished with silicon carbide paper and submitted to air abrasion using 50 μm aluminum oxide particles (Al2O3) under 4 bar pressure. Zirconia disks were randomly assigned to four groups (n=10): (G1) ResiCem luting cement + Porcelain Primer, (G2) ResiCemluting cement only, (G3) Clearfil Esthetic Cement + Clearfil Ceramic Primer and (G4) Clearfil Esthetic Cement only. The luting cements were prepared according to manufacturers’ recommendations and inserted in an elastomeric mold positioned onto a zirconia disc. Each specimen was photoactivated by 20 s. The specimens were stored at 100% relative humidity and 37ºC for 24 h. The ìsbs test was performed using universal testing machine at a crosshead speed of 0.5 mm/min. An optical microscope was used to analyze the failure modes and illustrative images were captured with a scanning electron microscope. The ìsbs data were analyzed by two-way ANOVA (p<0.05). Results: No significant difference was found among the four groups G1 (17.4±6.8), G2 (17.1±5.5), G3 (15.6±5.5) and G4 (14.2±3.5), all of which showed 100% of adhesive failures. Conclusions: CP showed no increase in the ìsbs between zirconia-based ceramic and resin luting cements.

Apical and cervical displacement produced by hand and engine-driven stainless steel and nickel-titanium instruments in simulated curved root canal

The purpose of this study was evaluate the occurrence of displacement on the apical and cervical thirds of artificial curved root canals with 30° of curvature, comparing the use of stainless steel hand and oscillatory files with nickel-titanium (NI-TI) hand, rotary and oscillatory files. Methods: Seventy artificial curved root canals were divided into 7 groups (n=10). All canals were prepared with sizes 15to 40 instruments at the working length according to a crown-down technique. The amount of material removed in the curved portion of the simulated canals at2 mm level outside and 11 mm inside was measured. Data were analyzed statistically by ANOVA and Tukey’s test (p<0.05). Results: There was statistically significant differences (p<0.05) at 2 mm level between NI-TI and steel stainless groups. At 11 mm, statistically significant differences (p<0.05) were observed between the groups that used rotary systems (5 and 6) and the remaining groups. Conclusions: The most centered preparations were those belonging to groups 5 and 6, at both levels. Root canal preparation with NI-TI files yielded better results than the stainless steel files especially when mechanically activated.

Pastas de prova em laminados cerâmicos: aplicação clínica para alcançar o resultado estético / Try-in pastes for porcelain laminate veneers: an esthetic achievement for esthetic results

Na odontologia restauradora, o mimetismo das restaurações em cerâmica é alvo de interesse considerável entre os profissionais, na reconstrução de elementos dentais ou modificações de forma e cor. A seleção de cores é uma etapa crítica do tratamento restaurador, especialmente em dentes anteriores, sendo o conhecimento das propriedades ópticas dos materiais e da estrutura dental de extrema importância para o sucesso da restauração final. Esta descrição clínica mostra a importância da escolha da cor do cimento resinoso na confecção de restaurações cerâmicas em dentes anteriores, com uso de pastas de prova

Mimicking restorations are desireable in Restorative Dentistry when teeth are being reconstructed or when shade and contour are be changed by restorations. Shade selection is a critical step in restorative treatment, especially in anterior dentition, and expertise on optical properties and tooth substrate is extremely important for the success of the final restoration. The purpose of this clinical guide is showing the significance of shade selection of resin cement for anterior ceramic restorations, by using try-in pastes

Dual resin cement knoop hardness after different activation modes through dental ceramics

This study investigated the influence of ceramic compositions on Knoop Hardness Number (KHN) immediately and 24 h after polymerization and the effect of activation modes on the KHN of a resin cement. Ten Panavia F 2.0 resin cement discs were activated either directly using curing light, or chemically without light, or through 1.2-thick ceramic discs. The following ceramics were evaluated: Duceram, Cergogold, IPS Empress, IPS Empress 2, Procera, Cercon, In Ceram Alumina and In Ceram Zirconia. The KHN was obtained immediately and after 24-h testing time. Two-way ANOVA and Tukey's test were performed for statistical analysis (p<0.05). Direct activation showed higher KHN than activation through ceramics and chemical activation for both immediate and 24-h post activation. The KHN for 24-h post activation time was higher than that of the immediate post activation time except for the direct activation mode. The glass and di-silicate based ceramics showed higher KHN than alumina- and zirconia-based ceramics, immediately and after 24-h. The reinforced and opaque ceramics had the lowest KHN. The ceramic composition resulted in light attenuation, lower polymerization and lower KHN, and the 24-h testing time promoted an improvement of KHN except for direct activation mode.

Este estudo investigou a influência de composições de cerâmica no número de dureza Knoop (KHN), imediatamente e 24 h após a polimerização; e o efeito de modos de ativação na KHN de um cimento resinoso. Dez discos de cimento resinoso Panavia F 2.0 foram ativados diretamente usando uma fonte de luz, ou quimicamente sem luz, ou através de discos de cerâmica com espessura de 1,2 mm. As cerâmicas avaliadas foram Duceram, Cergogold, IPS Empress, IPS Empress 2, Procera, Cercon, In Ceram Alumina e In Ceram Zirconia. O KHN foi obtido nos tempos imediatamente e após 24 h. Os testes ANOVA two-way e Tukey foram realizados para a análise estatística (p<0,05). A ativação direta apresentou maiores KHN que a ativação através das cerâmicas e ativação química, para ambos os tempos testados imediatamente e após 24 h. O KHN para o tempo de ativação testado após 24 h foi superior que o tempo imediatamente, exceto para o modo de ativação direto. As cerâmicas à base de vidro e di-silicato apresentaram KHN superiores que as cerâmicas à base de alumina e zircônia, imediatamente e após 24 h. As cerâmicas mais reforçadas e opacas resultaram um dos menores KHN. A composição da cerâmica resulta em atenuação de luz, menor polimerização e menor KHN; e o tempo de 24 h testado promove uma melhora no KHN, exceto para o modo de ativação direto.

Effect of surface treatment and storage on the bond strength of different ceramic systems

Aim: The aim of this study was to evaluate the micro shear bond strength of different ceramic systems – IPS Empress 2, Cergogold, In-Ceram Alumina and Cercon - and a dual luting agent. Methods: Twelve specimens of each ceramic were fabricated and divided according different surface treatments: Group 1: No additional treatment was applied to the ceramic surface; Group 2: Ceramics were etched with 9.5% hydrofluoric acid; Group 3: specimens treated with airborne particle abrasion for each ceramic system in accordance with manufacturer’s instructions (n=20). The tests were performed after 24 h or after water storage for 6 months. Data were then assessed statistically using the 3-way ANOVA and the Tukey’s test (P<0.05). Results: For Cergogold and IPS Empress 2 systems, the treatments performed with airborne particle abrasion and hydrofluoric acid showed no significant differences from each other, and both were superior to the groups without treatment. For Cercon and In-Ceram ceramics, no differences were found among the groups (P<0.05). When the surface was treated with hydrofluoric acid, the highest bond strength was found to IPS Empress 2 in the 6-month storage period (P<0.05). Conclusion: Lower bond strength values were only observed with IPS Empress 2 ceramic for the control group in the 6-month storage (P<0.05).

O condicionamento ácido prévio ainda é indispensável para a odontologia adesiva? / Is previous total etching still indispensable for the adhesive dentistry?

O objetivo deste trabalho foi avaliar as características dos sistemas adesivos disponíveis atualmente considerando a aplicação ou não do condicionamento prévio com ácido fosfórico. O conhecimento das estruturas e o tratamento adequado do substrato dental são fundamentais para utilização dos adesivos convencionais. Os sistemas adesivos autocondicionantes possuem técnica simplificada dispensando o condicionamento ácido prévio. O profissional deverá ter conhecimento dos mecanismos de adesão ao substrato dental, experiência clínica e domínio da técnica de aplicação do adesivo escolhido. O condicionamento ácido prévio não deve ser considerado indispensável na Odontologia adesiva atual.

Variação da força de resistência à micro-tração de fragmentos de ossos corticais preservados em diversos meios e a fresco: estudo experimental em coelhos / Variation of the resistance force to the micro-traction of fragments of cortical bones preserved in several means and fresh: Experimental study in rabbits

Devido ao crescente uso dos aloenxertos nas cirurgias ortopédicas, há a necessidade do conhecimento de suas características biomecânicas ao longo do tempo de preservação. O presente trabalho consistiu na análise da força de resistência à micro-tração de amostras de ossos corticais de coelho preservadas em diversos meios por até 180 dias e a fresco. Os resultados revelaram que a resistência e o tempo de preservação apresentaram uma relação inversamente proporcional, significando que, quanto maior o tempo de preservação, menor a resistência física avaliada no ensaio biomecânico de resistência à micro-tração. Dos meios utilizados, a glicerina apresentou menores valores quanto ao teste de resistência, demonstrando, após 30 dias de preservação, apenas 24,58 por cento da força presente no osso a fresco e, aos 180 dias, 1,76 por cento. As amostras submetidas à autoclavagem também demonstraram baixos valores ao final do experimento, quando permaneceram com apenas 12,31 por cento da força presente no osso a fresco. Os ossos preservados em plasma homólogo, líquido de dakin e aqueles criopreservados apresentaram os melhores índices de resistência ao final do experimento, permanecendo, respectivamente, com 82,47; 70,34 e 66,72 por cento da força máxima quando comparados com a resistência dos ossos frescos. Concluiu-se que a escolha do método e o tempo de preservação interferiu diretamente na biomecânica dos ossos corticais, promovendo a diminuição da capacidade de resistência à tração ao longo do período de preservação.

Due to the increasing use of cortical bone allografts in orthopedic surgeries, de knowledge of its biomechanics characteristics during preservation time is needed. The present study consisted in the analyses of the resistance power to the micro-traction of samples of rabbit cortical bones preserved in several means for up to 180 days and fresh. The results showed that the resistance and the preservation time presented an inversely proportional relation, meaning that, the longer the time of preservation, the shorter the physical resistance evaluated in the biomechanical rehearsal of resistance to the micro-traction. The glycerin has presented lower values in relation to the resistance test, showing, after 30 days, only 24.58 percent of the present power in the fresh bone, and by 180 days, 1.76 percent. The samples submitted to autoclavation also showed low values by the end of the experiment, while they remained with just 12.31 percent of the power present in the fresh bone. The bones preserved in homologous plasma, Dakin liquid and the ones cryopreserved showed the best levels of resistance at the end of the experiment, remaining, respectively with 82.47, 70.34 and 66.72 percent of the maximum power, while compared with the resistance of the fresh bones. The conclusion is that the choice of methodology and time of preservation interfered directly in the biomechanics of the cortical bones, promoting decrease of the resistance capacity to the traction along the period of preservation.

A influência do clareamento dental na resistência de união na interface resina-esmalte / The influence of tooth bleaching on the bond strength of resin-enamel interdaces

Redução na resistência de união depois de clareamento tem sido publicado, contudo, o efeito do clareamento na resistência de união com o esmalte utilizando adesivos de três passos que incluem aplicação de ácido fosfórico não tem sido amplamente reportada. Esse trabalho avaliou a influência do clareamento dental na adesividade de restaurações de resina composta em esmalte. Incisivos bovinos foram submetidos ao clareamento com peróxido de carbamida (PC) a 37% e peróxido de hidrogênio (PH) a 35%, obtidos em farmácia de manipulação. Em seguida os dentes foram fixados em anéis de PVC, recebendo um cilindro de resina composta com 3mm de altura e 5mm de diâmetro na face vestibular. Utilizou-se o adesivo Scotchbond Multipurpose 3M e a resina composta Z100 - 3M. Uma fita de aço envolveu o cilindro de resina sob cisalhamento com velocidade de 0,5mm por minuto e célula de carga de 50kgf. Foram obtidos os seguintes resultados: Grupos controles restaurados sem clareamento: PHS:8,52MPa; PCS:8,30MPa. Imediatamente após o clareamento PHI:3,15MPa;PCI:4,10MPa. Após 24 horas PH24:5,68MPa; PC24:7,38MPa. Após 48 horas PH48:7,69MPa; PC48:6,93MPa. Após 7 dias PH7D:8,60MPa; PC7D:7,24MPa. Após 15 dias PH15D:7,36MPa; PC15D:9,08MPa. Após 21 dias PH21D:7,92MPa; PC21D:7,62MPa. Após aplicar o teste de Tukey (p<0,05), os subgrupos PHI, PH24, PCI apresentaram valores estatisticamente inferiores aos demais, o que implica um tempo necessário mínimo entre o clareamento e a restauração de resina composta, de 48 horas para PH (35%) e de 24 horas para PC (37%)

The aim of this study was to evaluate the influence of bleaching on the shear bond strength between a composite resin and enamel. One hundred forty bovine teeth were assigned according to the bleaching material used: 37% Carbamide peroxide (PC) and 35% hydrogen peroxide (PH), both obtained in a compounding pharmacy. Within each material, the teeth were divided in 7 groups (n=10 ) according with the time between bleaching and restoration: group 1 - control without bleaching; group 2 - immediately after bleaching; group 3 - twenty four hours; group 4 - forty eight hours; group 5 - seven days; group 6 - fifteen days and group 7 - twenty one days. The teeth were embedded with auto polymerizing acrylic resin in polyvinyl chloride (PVC) tubes. The adhesive system (Scotchbond Multipurpose-3M) was applied, and a cylinder of composite resin (Z100-3M) with 3 mm of height and 5 mm in diameter was bonded on each tooth labial surface. The shear bond strength test was performed in a universal testing machine at a crosshead speed of 0.5 mm/min using a load cell of 50kgf. Data were analyzed with 1-way analysis of variance and Tukey's test. Results: group 1: PH- 8.52MPa, PC- 8.30MPa; group 2: PH- 3.15MPa, PC-4.10MPa; group 3: PH-5.68MPa, PC-7.38MPa. Group 4: PH-7.69MPa, PC-6.93MPa; Group 5: PH-8.60MPa, PC-7.24MPa; Group 6: PH-7.36MPa, PC-9.08MPa and group 7: PH-7.92MPa, PC-7.62MPa. The data showed that a delay in bonding procedures is recommended. A minimum time to perform the restoration after bleaching withPH (35%) is 48 hours and withPC (37%) 24 hours

Efeito do selamento dentinário imediato e de materiais restauradores provisórios na resistência de união à dentina / Effect of immediate dentin sealing and provisional restorations on bond strength to dentin

Objetivo: O objetivo do estudo foi avaliar, in vitro, o efeito da técnica do selamento dentinário imediato com um sistema adesivo de 5º geração, e da aplicação intermediária de dois materiais provisórios, na resistência de união à tração sobre a dentina. Materiais e método: A coroa de 75 dentes incisivos bovinos foram incluídas em resina acrílica quimicamente ativada, sendo a superfície vestibular desgastada até exposição da dentina. A superfície dentinária recebeu acabamento com lixas de granulação 400 e 600, sendo os dentes divididos em 5 grupos (n = 15): Grupo 1: Single Bond (controle); Grupo 2: Temp Bond NE + Single Bond; Grupo 3: Single Bond + Temp Bond NE + Single Bond; Grupo 4: Fermit + Single Bond; Grupo 5: Single Bond + Fermit + Single Bond. Os grupos 3 e 5 reproduziram a técnica de selamento imediato da dentina. Um cone de resina composta (Z250) foi construído sobre o adesivo. Após armazenamento por 24 horas a 37ºC em água destilada, os corpos-de-prova foram submetidos ao teste de resistência à tração em máquina de ensaio universal. Resultados: De acordo com a Análise de Variância, não houve diferença estatisticamente significativa nos valores médios de resistência à tração entre os grupos (p > 0,05): grupo 1 (16,84 MPa); grupo 2 (14,27 MPa); grupo 3 (17,27 MPa); grupo 4 (14,87 MPa); grupo 5 (12,97 MPa). Conclusão: A técnica de selamento imediato da dentina com o sistema adesivo Single Bond, assim como os materiais provisórios Temp Bond NE e Fermit, não influenciaram significativamente os valores de resistência de união à dentina.

Effect of refrigeration on bond strength of self-etching adhesive systems

The purpose of this study was to investigate the tensile bond strength to dentin of three self-etching adhesive systems at refrigerated and room temperatures. Seventy-eight bovine incisors were embedded in self-cured acrylic resin, abraded on a water-cooled lathe and polished with 400- and 600-grit sandpapers to obtain standard dentin surfaces. The specimens were randomly assigned to 6 groups (n=13). Clearfil SE Bond, AdheSE and One-Up Bond F adhesive systems at refrigerated (4°C) and room temperatures (23°C) were applied to dentin according to the manufacturers' instructions. A truncated composite resin (Herculite XRV) cone was bonded to dentin surface. The specimens were stored in distilled water at 37°C for 24 h and submitted to tensile bond strength testing at a crosshead speed of 0.5 mm/min. Means in MPa were analyzed statistically by Student's t-test at 5 percent significance level. No statistically significant differences (p>0.05) were found between the adhesive systems applied at refrigerated and room temperatures. In conclusion, no adverse effects on tensile bond strength were observed when self-etching adhesive systems were used after being taken directly from the refrigerated storage.

O objetivo deste trabalho foi avaliar a resistênciade união à dentina de três sistemas adesivos autocondicionantes quando estes se encontravam refrigerados ou à temperatura ambiente. Setenta e oito incisivos bovinos foram embutidos em resina acrílica autopolimerizável, desgastados em um torno mecânico sob refrigeração à água, polidos com papel abrasivo de granulação 400 e 600 para obter uma superfície plana em dentina. Os corpos-de-prova foram divididos aleatoriamente em 6 grupos (n=13). Os sistemas adesivos Clearfill SE Bond, AdheSE and One-Up Bond F foram aplicados sobre a dentina de acordo com as instruções dos fabricantes, estando os mesmos refrigerados (4°C) ou à temperatura ambiente (23°C), seguido da união da resina composta Herculite XRV formando um cone invertido. Os corpos-de-prova foram armazenados em água destilada a 37°C por 24 h e submetidos a ensaios de resistência à tração com velocidade de 0,5 mm/min. As médias (em MPa) foram analisadas estatisticamente pelo teste t de Student com nível de significância de 5 por cento. Não houve diferença estatisticamente significante (p>0.05) entre os valores de resistência de união quando os sistemas adesivos encontravam-se refrigerados ou à temperatura ambiente. Concluiu-se que nenhum efeito adverso foi observado na resistência à tração quando os sistemas adesivos foram utilizados imediatamente após a remoção da armazenagem sob refrigeração.

Avaliação in vitro das distorções promovidas em canais radiculares artificiais curvos comparando o preparo cervical com limas de níquel-titânio acionadas a motor e brocas de Gates-Glidden / Evaluation in vitro of changes promoted in simulated root canals curved comparing the cervical preparation with nickel-titanium files actived by a motor and drills of gates-glidden

A instrumentação de canais radiculares curvos resulta, por vezes, na formação de acidentes e deformações. Neste trabalho, comparou-se as alterações promovidas em 20 canais radiculares artificiais curvos, de aproximadamente 30 graus de acordo com a metodologia proposta por Schneider (1971), após preparo com limas de níquel-titânio Pow-R, acionadas a motor de taper 0.4, para realização do preparo cervical, e taper 0.2 para o preparo apical (grupo 1), preparo cervical com brocas de Gates-Glidden, e na porção curva limas Pow-R taper 0.2 (grupo 2). As imagens pré e pós-instrumentação foram sobrepostas, e analisadas através do programa Image Tool. Avaliaram-se as distâncias desgastadas, no nível de 13 milímetros aquém do final apical dos canais simulados, para o lado interno; área desgastada externa da parte curva (11 milímetros) e área desgastada interna da parte curva (11 milímetros). Os resultados mostraram, que os preparos para o grupo 1 desgastaram maiores extensões, na região apical, lado externo da curvatura em relação aos canais simulados do grupo 2, significante ao nível de 1%, evidenciando maior tendência para formação de "zip"; os preparos para o grupo 2 desgastaram maiores extensões, na região apical, lado interno da curvatura em relação aos canais simulados do grupo 1, significante ao nível de 1%. As distâncias desgastadas no nível de 13 milímetros foram significativamente maiores ao nível de 1%, para o grupo 2 em ralação ao grupo 1. Pelas médias de desgastes, lado interno e externo, os preparos para o grupo 1 ficaram mais centrados em relação aos do grupo 2

Influência da reutilização da liga Ni-Cr na resistência de união com a cerâmica / Influence of the recast of Ni-Cr alloy in the bond strength to ceramic

As ligas de Ni-Cr são muito empregadas para confecção de restaurações metalocerâmicas, e o reaproveitamento de liga por meio de refundição poderia amenizar custos laboratoriais. O objetivo do estudo foi verificar a influência do reaproveitamento da liga Ni-Cr VeraBond 2 na resistência de união com a cerâmica feldspática Vita Omega 900. Foram confeccionadas 150 tiras metálicas em liga de Ni-Cr com 25 x 3 x 0,5 mm empregando diferentes porcentagens de liga nova e reutilizada: Grupo 1 - apenas liga nova; Grupo 2 - 75 por cento de liga nova e 25 por cento reutilizada; Grupo 3 - 50 por cento de liga nova e 50 por cento de reutilizada; Grupo 4 - 25 por cento de liga nova e 75 por cento de reutilizada; Grupo 5 - 100 por cento reutilizada. A cerâmica foi aplicada na região central das tiras. Metade dos corpos-de-prova foram temociclados, sendo todos submetidos ao teste de flexão de três pontos em máquina de ensaio universal EMIC DL 2000. Os resultados foram analisados pela ANOVA e teste de Tukey (P < ou = 0,05). Houve significância apenas para o fator porcentagem de liga, sendo que a termociclagem não influenciou a união metal/cerâmica. Os maiores valores foram obtidos com a liga 100 por cento nova (35,99 MPa) e 25 por cento reutilizada (31,80 MPa), seguido da liga 50 por cento reutilizada (25,14 MPa), e 75 por cento reutilizada (21,41 MPa), sendo os menores valores para a liga 100 por cento reutilizada (17,51 MPa). Com as ligas 100 por cento nova, 25 por cento e 50 por cento reutilizadas, a resistência de união metal/cerâmica situou-se dentro dos valores aceitáveis para utilização clínica

Cerâmicas hidrotérmicas: o que são ? / Hydrothermal ceramics: what are those ?

As cerâmicas odontológicas são um dos materiais que mais têm evoluído nas últimas décadas. Uma das inovações foi o desenvolvimento das cerâmicas hidrotérmicas, que represetam o surgimento de uma nova tecnologia em material cerâmico. O presente trabalho é uma revisão de literatura sobre as cerâmicas hidrotêrmicas, e relaciona sua composição química com determinadas características importantes dos materiais, como capacidade de desgaste do dente antagonista, resistência, durabilidade e estética.

Avaliação da dureza e rugosidade superficial da cérâmica feldspática glazeada e polida / Avaliation of the superficial hardness and roughness of glazed and polished feldspathic ceramic

O objetivo deste trabalho foi avaliar a dureza e rugosidade superficial da cerâmica feldspática Duceram-Plus (Degussa) glazeada e polida após simulação de ajuste oclusal. Foram confeccionados 20 discos (7 mm de diâmetro x 2 mm de espessura) de cerâmica, sendo realizado o autoglazeamento. A rugosidade superficial e a dureza Vickers foram mensurados em cada disco de cerâmica. A seguir, os mesmos foram submetidos à simulação de ajuste oclusal com ponta diamantada de granulação fina em alta rotação sob refrigeração, seguido de acabamento e polimento com o conjunto de abrasivos Edenta (Labor Dental). Nova avaliação da rugosidade superficial e dureza Vickers foi realizada. De acordo com os resultados submetidos à análise de variância e ao teste de Tukey (p < 0,05) concluiu-se que, para a cerâmica polida, tanto a rugosidade (0,3234 Mm) como a dureza Vickers (553,2 VHN) foram estatisticamente superiores à rugosidade (0,1681 Mm) e à dureza Vickers (513,1 VHN) da cerâmica glazeada.

Effect of refrigeration on tensile bond strength of three adhesive systems

O objetivo deste trabalho foi avaliar a resistência à tração sobre a dentina de três sistemas adesivos quando estes se encontravam refrigerados e à temperatura ambiente. Noventa dentes bovinos foram embutidos em resina acrílica autopolimerizßvel, desgastados em um torno mecânico sob refrigeração à água, polidos com papel abrasivo de granulação 400 e 600 para obter uma superfície plana em dentina, e divididos aleatoriamente em seis grupos (n=15). Os sistemas adesivos Scotchbond Multi-Purpose, Single Bond e Prime & Bond NT foram aplicados sobre a dentina de acordo com as instruções dos fabricantes, estando os mesmos refrigerados (4°C) ou à temperatura ambiente (23°C), seguido da união da resina composta Z 100. Os corpos-de-prova foram armazenados em água destilada a 37°C por 24 horas e submetidos ao teste de resistência à tração em mßquina de ensaio universal (EMIC DL-2000) com velocidade de 0,5 mm/min. Os valores obtidos foram submetidos à análise de variância e ao teste de Tukey. Não houve diferença estatística nos valores de resistência de união quando os sistemas adesivos encontravam-se refrigerados ou à temperatura ambiente. Scotchbond Multi-Purpose e Single Bond demonstraram resistência à tração significativamente superior em relação ao Prime & Bond NT na temperatura ambiente e refrigerada (p<0,01). Nenhuma diferença estatística foi encontrada entre o Scotchbond Multi-Purpose e Single Bond. Nenhum efeito adverso foi observado na resistência à tração quando utilizados os sistemas adesivos imediatamente após a remoção da armazenagem sob refrigeração.